Solid stainless steel welding wire

APPLICATIONS

Overlay of carbon and low-alloy steels for resistance to corrosion, erosion, or abrasion. 410 has higher hardness and is used in valve seats to obtain better galling resistance. Normally to obtain adequate ductility, preheat and post-weld heat-treatment are required.

PROPERTIES

410 is a martensitic stainless steel that is heat-treatable. It has a nominal weld metal composition of 12% Chromium. These weld deposits are air-hardenable that can normally be heat-treated after welding.

CLASSIFICATION

AWS

A 5.9: ER 410

EN ISO

14343-A: G Z 13

DIN: W.Nr.

1.4009

DIN

8556: SG-X 8 Cr 14

SUITABLE FOR

For welding or repairing 12% Cr air-hardenable stainless steels like types 410, 416, 420, 431 and cast C-15, W.Nr: 1.4008, 1.4000, 1.4006, X8Cr14, X6Cr13, X10Cr13 and cast steels.

APPROVALS

CE approved

WELDING POSITIONS:

WELD DEPOSIT WEIGHT % (TYPICAL)

C	Mn	Si	Cr	Ni	Mo	Cu
< 0,12	< 0,60	< 0,50	12-13,5	< 0,60	< 0,75	< 0,40

MECHANICAL PROPERTIES

Heat	R_P0,2	Rm	A5	Impact Energy (J) ISO-V			Hardness
Treatment	(N/mm²)	(N/mm²)	(%)	-20°C	-40°C	-60°C	HRc / HB
AW							35 HRc
PWHT 680C/8hr	>450	>650	>15				180 HB 30

PWHT: Post weld heat treatment

WELDING PARAMETERS PACKING

Welding Parameters			Packing
D (mm)	Voltage (V)	Current (A)	spool type	kg / 6pack	kg / pallet
1,0			K-300 / Drum	15 / 250	1080 / 1000
1,2			K-300 / Drum	15 / 250	1080 / 1000
1,6			K-300 / Drum	15 / 250	1080 / 1000