Filler Metals

BrazeTec S 2 BrazeTec S 2

Technical Data Sheet

BrazTec S 2

 

TD BT 0604 E.01

 

Standard

CP 105 acc. DIN EN 1044 (L-Ag2P acc. DIN 8513)

B-Cu92PAg-645/825 acc. ISO 3677

 

Nominal composition in wt.-%                       Cu remainder; Ag 7; P 6,3

Permited impurities (weight-%):

AI 0,01; Bi 0,030; Cd 0,025; Pb 0,025; Zn 0,05; Zn + Cd 0,05; Total impurities 0,25

 

Technical data                             

Melting range                                                      app. 645-825°C           (DIN EN 1044)

Working temperature                                           app. 740°C                 (DIN EN 1044)

Density                                                               app. 8,1 g/cm3            (DIN EN 1044)

Tensile strength acc. DIN 8525                              with Cu: 250 MPa

Elongation                                                           app. 5 %

Eletrical Conductivity                                             app. 4,0 m/Ωmm2

Operating temperature of brazed joint                    max. 150°C (without loss in strentg)

 

Standard delivery form*

Wire:         1,0 - 1,5 - 2,0 mm Ø

Rods:        1,5 - 2,0 - 3,0 mm Ø, 500 mm length

Ribbon: 0,1/ 0,2/ 0,3/ 0,4 mm thickness and 70 mm width

Preforms: rings, shaped parts, sections, stemped parts, lamina, discs, perforated plates

*Other delivery forms on request

 

Application

BrazeTec S 2 is a phosphorous-containing brazing alloy with good flow characteristics. The brazing alloy is suitable for joining copper to copper or copper-based materials. Due to its phosphorous content, you have not to use an additioal flux for brazing only copper to copper. This brazing alloy is not allowed to be used if sulfur containing medias may have contact with the joint during operating. Futher it is not allowed to use this alloy for joining steels (Fe) or materials containing iron, nickel and cobalt as brittle phases will be formed in the joint.

In refrigation and air conditioning industries BrazeTec S 2 can be used for service temperatures down to -50°C.

It can be used for brazing with flame, with induction heating and in a furnace under protective atmospheres.

Typical applications are found e.g. in the electric industry and for the refrigaration and air conditioning industry.